Boron doping of silicon using coalloying with aluminium
Publication
Publication
Appl. Phys. Lett. , Volume 65 p. 2792- 2794
We present a new technique for boron (B) doping of silicon. In this letter we show that a B doping profile of more than 2 µm thickness with a maximum active doping concentration of 3X1019 cm-3 can be formed by a fast (<1 min) alloying process at a temperature of 850 ³C. Thick-film aluminum is used to obtain an alloying and epitaxial regrowth process in accordance with the Al-Si phase diagram. The atomic concentration profile of the B- and Al-doped Si layer was determined by secondary ion mass spectrometry. The active doping concentration was measured with an automatic electrochemical capacitance/voltage profiler. By the addition of B to the Al paste, the epitaxially regrown layer is doped with B and Al to the solid solubility of these elements in Si at the particular regrowth temperature. The applicability of this fast low temperature B doping process in Si solar cell processing is discussed.
Additional Metadata | |
---|---|
doi.org/10.1063/1.112992 | |
Appl. Phys. Lett. | |
Sinke, W., Leguijt, C., Weeber, A. W., Alkemade, P. F. A., & Verhoef, L. A. (1994). Boron doping of silicon using coalloying with aluminium. Appl. Phys. Lett., 65, 2792–2794. doi:10.1063/1.112992 |